Vivid Cure™ – Liquid Optically Clear Adhesives (LOCA) 806-VLS

Vivid Cure™ 806-VLS

LOW STRESS UV CURE ADHESIVE 

Fast curing, water white clear, urethane acrylate designed for utilization as an LCD interface adhesive. This product is a soft, flexible, low modulus polymer that provides a high amount of bond strength without imparting stress. This is a non-yellowing adhesive that exhibits excellent resistance to moisture.

APPLICATIONS FEATURES SUBSTRATES
Touch Screen Display RoHS & REACH Compliant Plastics
LCD GB 33372-2020 Compliant Glass
 Large Format Displays Non-Yellowing, No-Haze Metals
Consumer Displays Low-Stress Adhesive
Medical Devices Ultra-Low Shrinkage
UVA Curable

Typical Properties of HumiSeal® Vivid CureTM 806-VLS

Chemical Class UV Acrylate
Appearance Clear
 Viscosity @ 25°C, Spindle 5 @ 20 RPM, cps 1,900 to 3,100
Specific Gravity   0.87-0.93
Cleanup Solvent Isopropyl alcohol

UV Curing Guidelines*

HumiSeal Vivid Cure™ 806-VLS adhesive has been formulated to allow flexibility in the curing process. HumiSeal Vivid Cure™ 806-VLS can be cured using 395nm LED systems. The table below details minimum dosage values required to properly crosslink HumiSeal Vivid Cure™ 806-VLS.

“Note, adhesive thickness range of 700 – 750 microns was used during the development of the minimum required dosage values recommended below. If a different adhesive thickness is used, process adjustments may be required.”

 

Vivid CureTM  806-VLS Recommended Minimum Dose (J/cm2) Requirements

Wavelength (nm)  UVV
395nm 5.0

Values measured with an EIT Powerpuck II

* These values are for guidelines only and not meant to be used as a specification

It is recommended that you contact HumiSeal technical support to discuss your application and review the required recommended minimum cure requirements.

 

Typical Properties of Cured Material**

Tensile Modulus @ -60°C, MPa 100 to 500
Glass Transition Temperature (Tg), °C -40 to -45
Linear Shrinkage, % < 1
Refractive Index 1.459 to 1.470
Haze, %, per ASTM D1003 < 0.2
Total Luminous Transmittance, %, per ASTM D1003 > 99
Color Coordinate, b* 0.03
Dielectric Constant / Dissipation Factor @ 200 KHz 2.94 / 0.045
Dielectric Constant / Dissipation Factor @ 400 KHz 2.65 / 0.044
Dielectric Constant / Dissipation Factor @ 800 KHz 2.86 / 0.042
Dielectric Constant / Dissipation Factor @ 1 MHz 2.79 / 0.046
Operating Temperature Range, °C -50 to 125

**All properties given are typical values and are not intended for use in preparing specifications.

Storage & Handling

HumiSeal Vivid Cure™ 806-VLS should be stored between 8°C – 28°C in tightly closed, light-blocking containers, away from direct sunlight. Keep from freezing. Allow material to equilibrate to process area temperature for 24 hours before use. Please refer to product labeling for shelf-life information. While the material can be heated to facilitate degassing prior to use, this operation should be conducted only on the amount of adhesive to be immediately used. Multiple heating cycles of the bulk container or elevated temperature storage of HumiSeal Vivid Cure™ 806-VLS should be avoided. Consult SDS for full safety information.