Silicone 1C49LVF
HumiSeal® 1C49LVF conformal coating is:
- silicone based
- very fast curing
- fluoresces under UV light
- room temperature, moisture cure
- single component
- high solids
HumiSeal 1C49LVF conformal coating has:
- No VOCs or solvent
- excellent environmental resistance and moisture resistance
- RoHS directive 2015/863/EU
- recognized under UL file number E105698
Application of 1C49LVF Silicone Conformal Coating
Conformal coatings can be successfully applied to substrates that have been cleaned prior to coating and also to substrates assembled with low residue “no clean” materials. Users should perform adequate testing to confirm compatibility between the conformal coating and their particular assembly materials, process conditions and cleanliness level. Please contact a HumiSeal representative for additional information
1C49LVF is designed for application without additional thinning. Solvents or other thinners should not be mixed with 1C49LVF. 1C49LVF may be applied by spray, brushing, flow coating or dipping. The time required to reach a tack-free state is dependent on ambient conditions such as temperature and relative humidity. The processing guidelines contained in this document were obtained with an ambient relative humidity of 50%.
Spraying
HumiSeal® 1C49LVF may be applied using conventional spraying equipment. Spraying should be done in an environment with adequate ventilation so that the vapor and mist are carried away from the operator. The use of thinner is not required or recommended for HumiSeal® 1C49LVF.
Brushing
Uniformity of the film depends on the component density and the operator’s technique.
| Product Specification | |
| Density, per ASTM D1475 | 0.97 ± 0.03 g/cm³ |
| Min. Solids Content, % by weight per Fed-Std-141, Meth. 4044 | 50 % |
| Viscosity, per Fed-Std-141, Meth. 4287 | 550 ± 250 centipoise |
| VOC | 0 grams/liter |
| Recommended Coating Thickness | 50 – 200 microns |
| Drying Time to Handle per Fed-Std-141, Meth. 4061 | <10 min |
| Recommended Curing Conditions | 24 hrs @ RT or 20 min @ 76°C* |
| Time required to Reach Optimum Properties | 7 days |
| Recommended Stripper | HumiSeal Stripper 1091 |
| Shelf Life at Room Temperature, DOM | 12 months |
| Thermal Shock, 50 cycles per MIL-I-46058C | -65°C to 200°C |
| Glass Transition Temperature – DSC | < -65°C |
| Storage Modulus – DMA | 10.2 MPa @ -40ºC 4.7 MPa @ 25ºC 4.0 MPa @ 80ºC |
| Flammability, per UL94 | V-0 |
| Dielectric Withstand Voltage, per MIL-I-46058C | >1500 volts |
| Dielectric Breakdown Voltage, per ASTM D149 | 7000 volts |
| Dielectric Constant, at 1MHz and 25°C per ASTM D150-98 | 2.5 |
| Dissipation Factor, at 1MHz and 25°C per ASTM D150-98 | 0.01 |
| Insulation Resistance, per MIL-I-46058C | 3.9 x 1012 ohms |
| Moisture Insulation Resistance, per MIL-I-46058C | 1.94 x 1010 ohms |
| Fungus Resistance, per ASTM G21 | Passes |
* Place an open pan of water in the oven during curing