HumiSeal® UV40HV conformal coating is:
- single component
- high solids/high viscosity
- UV curable
- acrylated polyurethane
HumiSeal UV40HV conformal coating has:
- excellent chemical resistance, surface hardness, flexibility, and moisture resistance.
- secondary moisture cure mechanism for curing in the non-UV exposed shadowed areas
- fluoresces under UV light to allow for coating inspection
- can be applied by selective coating equipment.
- IPC-CC-830 and RoHS Directive 2011/65/EU compliant
Application of UV40HV Conformal Coating
Conformal coatings can be successfully applied to substrates that have been cleaned prior to coating and also to substrates assembled with low residue, “no clean” assembly materials. Users should perform adequate testing to confirm compatibility between the conformal coating and their particular assembly materials, process conditions and cleanliness level. Please contact HumiSeal® for additional information.
HumiSeal® UV40HV can be applied via standard selective coating equipment or by conventional hand spray equipment. The source air used for spraying must be dry (a dry inert gas is highly recommended) to prevent premature curing of the secondary cure mechanism. The spraying should be done with adequate ventilation so that the vapor and mist are carried away from the operator.
HumiSeal® UV40HV may be applied by brush for rework or touch up only. Brush must be cleaned with solvent promptly after use.
To flush equipment and clean uncured HumiSeal® UV40HV, non-alcohol based solvents should be used. HumiSeal® Thinner 521 or Thinner 521EU is recommended.
HumiSeal® UV40HV is a highly cross-linked UV cured coating. The cured film has a high degree of environmental and chemical resistance and will be more difficult to remove than traditional conformal coatings. Thermal displacement, mechanical abrasion and, where available, HumiSeal® Stripper 1100 are suitable options for rework of HumiSeal® UV40HV.
|Density||1.05 – 1.15 g/cm3|
|Minimum Solids Content||95 %|
|Viscosity, per Fed-Std-141, Meth. 4287||3700 ± 1300 centipoise|
|Recommended UV Cure*||See TDS for Details|
|Shelf Life at Room Temperature, DOM||12 months|
|Recommended Stripper **||HumiSeal® Stripper 1100|
|Thermal Shock, 50 cycles per MIL-I-46058C||-65°C to 125°C|
|Glass Transition Temperature – DSC||45°C|
|Coefficient of Thermal Expansion – TMA||85 ppm/°C Below Tg
197 ppm/°C Above Tg
|Dielectric Withstand Voltage, per MIL-I-46058C||>1500 volts|
|Dielectric Constant, at 1MHz and 25°C per ASTM D150-98||2.5|
|Dissipation Factor, at 1MHz and 25°C per ASTM D150-98||0.01|
|Insulation Resistance, per MIL-I-46058C||8.0 x 1014 ohms (800TΩ)|
|Moisture Insulation Resistance, per MIL-I-46058C||4.7 x 1010 ohms (47GΩ)|
|Fungus Resistance, per ASTM G21||Pass|
*Microwave UV cure ovens equipped with “H” style bulbs recommended
**Stripper 1100 is not available in the EU