UV40 Solar

UV40 Solar

HumiSeal® UV40 SOLAR conformal coating is:

  • single component
  • high solids
  • UV curable
  • acrylated polyurethane
  • no-yellowing with exposure to UV
  • meets requirements of SAA-J1960

HumiSeal UV40 SOLAR conformal coating has:

  • excellent chemical resistance, surface hardness, flexibility and moisture resistance.
  • secondary moisture cure mechanism for curing in the non-UV exposed shadowed areas
  • fluoresces under UV light to allow for coating inspection
  • can be applied by selective coating equipment.
  • recognized under UL File Number E105698
  • MIL-I-46058C qualified
  • IPC-CC-830 and RoHS Directive 2011/65/EU compliant

Application of UV40 SOLAR Conformal Coating

Conformal coatings can be successfully applied to substrates that have been cleaned prior to coating and also to substrates assembled with low residue, “no clean” assembly materials. Users should perform adequate testing to confirm compatibility between the conformal coating and their particular assembly materials, process conditions and cleanliness level. Please contact HumiSeal® for additional information.

Spraying
HumiSeal® UV40 SOLAR can be applied via standard selective coating equipment or by conventional hand spray equipment. The source air used for spraying must be dry (a dry inert gas is highly recommended) to prevent premature curing of the secondary cure mechanism.  The spraying should be done with adequate ventilation so that the vapor and mist are carried away from the operator. 

Brushing
HumiSeal® UV40 SOLAR may be applied by brush for rework or touch up only. Brush must be cleaned with solvent promptly after use.

Clean Up
To flush equipment and clean uncured HumiSeal® UV40 SOLAR, non-alcohol-based solvents should be used. HumiSeal® Thinner 521 or Thinner 521EU is recommended.

Rework
HumiSeal® UV40 SOLAR is a highly cross-linked UV cured coating.  The cured film has a high degree of environmental and chemical resistance and will be more difficult to remove than traditional conformal coatings.  Thermal displacement, mechanical abrasion and, where available, HumiSeal® Stripper 1100 are suitable options for rework of HumiSeal® UV40 SOLAR.

Product Specification
Density 1.06 g/cm3
Minimum Solids Content 95 %
Viscosity, per Fed-Std-141, Meth. 4287 650 ± 150 centipoise
Recommended Coating Thickness 25-125 microns
Recommended UV Cure* See TDS for Details
Shelf Life at Room Temperature, DOM 12 months
Thermal Shock, 50 cycles per MIL-I-46058C -65ºC to 125ºC
Glass Transition Temperature – DSC 45ºC
Coefficient of Thermal Expansion – TMA 85 ppm/ºC Below Tg
197 ppm/ºC Above Tg
Modulus – DMA 10364 MPa @ -40°C
4283 MPa @ 25°C
66 MPa @ 80°C
Dielectric Withstand Voltage, per MIL-I-46058C >1500 votls
Dielectric Constant, at 1MHz and 25°C per ASTM D150-98 2.5
Dissipation Factor, at 1MHz and 25°C per ASTM D150-98 0.01
Insulation Resistance, per MIL-I-46058C 8.0 x 1014 ohms (800TΩ)
Moisture Insulation Resistance, per MIL-I-46058C 4.7 x 1010 ohms (47GΩ)
Fungus Resistance, per ASTM G21 Pass

*Fusion “H” style bulb recommended

Other products in this chemistry include:


To view SDS files you need to Login or Request Access.