Urethane 1A33NS

HumiSeal® 1A33NS conformal coating is:

  • urethane chemistry
  • toluene free
  • chemically resistant
  • single component
  • contains no free isocyanates
  • RoHS directive 2015/863/EU
  • Recognized under UL File Number E105698

HumiSeal 1A33NS conformal coating has:

  • excellent moisture and environmental protection for printed circuit assemblies
  • fluorescence under UV light for ease of inspection

Application of 1A33NS Conformal Coating

Conformal coatings can be successfully applied to substrates that have been cleaned prior to coating and also to substrates assembled with low residue “no clean” materials. Users should perform adequate testing to confirm compatibility between the conformal coating and their particular assembly materials, process conditions and cleanliness level. Please contact a HumiSeal representative for additional information.

Dipping
Depending on the complexity, density and configuration of components on the assembly, it may be necessary to reduce the viscosity of HumiSeal 1A33NS with HumiSeal Thinner 521 in order to obtain a uniform film. Once optimum viscosity is determined, a controlled rate of immersion and withdrawal (typically, 5 to 15 cm/min) will further ensure even deposition of the coating and provide a uniform film. During application, evaporation of solvent causes an increase in viscosity that should be adjusted by adding small amounts of HumiSeal® Thinner 521. Viscosity in the dip tank should be checked regularly using a simple measuring device, such as a Zahn or Ford viscosity cup. 

Spraying
HumiSeal 1A33NS can be sprayed using conventional spraying equipment. Spraying should be done in an environment with adequate ventilation so that vapor and mist are carried away from the operator. The addition of HumiSeal® Thinner 521 is necessary to ensure a uniform spray pattern resulting in a pinhole-free film. The amount of thinner and spray pressure will depend on the specific type of spray equipment and operator technique. The recommended ratio of HumiSeal 1A33NS to HumiSeal Thinner 521 is 1:1 by volume; however, the ratio may need to be adjusted to obtain a uniform coating.

Brushing
HumiSeal 1A33NS may be brushed with a small addition of HumiSeal Thinner 521. Uniformity of the film depends on the component density and operator technique.

Product Specification
Density, per ASTM D1475 0.95 ± 0.02 g/cm3
Solids Content, % by weight per Fed-Std-141, Meth. 4044 44 ± 2 %
Viscosity, per Fed-Std-141, Meth. 4287 180 ± 20 centipoise
VOC 521 grams/lire
Recommended Coating Thickness 25 – 75 microns
Drying Time to Handle per Fed-Std-141, Meth. 4061 15 minutes
Optional Curing Conditions to Reach Optimum Properties 30 days at RT30 hours @ 76°C20 hours @ 88°C
Recommended Thinner (dipping, brushing) HumiSeal Thinner 521
Recommended Thinner (spraying) HumiSeal Thinner 521, 521EU
Recommended Stripper HumiSeal Stripper 1063
Shelf Life at Room Temperature, DOM 24 months
Thermal Shock, 50 cycles per MIL-I-46058C -65° to 125°C
Coefficient of Thermal Expansion – TMA 193 ppm/°C
Glass Transition Temperature – DSC 26°C
Modulus – DMA 27.2 MPa
Dielectric Withstand Voltage, per MIL-I-46058C >1500 volts
Dielectric Breakdown Voltage, per ASTM D149  7500 volts
Dielectric Constant, at 1MHz and 25°C per ASTM D150-98 3.6
Dissipation Factor, at 1MHz and 25°C per ASTM D150-98 0.03
Insulation Resistance, per MIL-I-46058C 2.0 x 1014 ohms (200TΩ)
Moisture Insulation Resistance, per MIL-I-46058C 1.6 x 1010 ohms (16GΩ)
CTI, PLC per UL746A @ 600 volts 0
Fungus Resistance, per ASTM G21 Passes