2A64

Urethane 2A64

HumiSeal® 2A64 conformal coating is:

  • Urethane chemistry
  • chemically resistant
  • two component
  • used in combination with Thinner 64

HumiSeal 2A64 conformal coating has:

  • excellent moisture and environmental protection for printed circuit assemblies
  • fluorescence under UV light for ease of inspection
  • MIL-I-46058C qualified
  • IPC-CC-830 compliant
  • RoHS Directive 2011/65/EC compliant.

Application of 2A64 Conformal Coating

Conformal coatings can be successfully applied to substrates that have been cleaned prior to coating and also to substrates assembled with low residue “no clean” materials.  Users should perform adequate testing to confirm compatibility between the conformal coating and their particular assembly materials, process conditions and cleanliness level.  Please contact HumiSeal® for additional information.

Mixing ratio of Part A to Part B is 1:1 by volume. Prior to application, HumiSeal® 2A64 Parts A and B should be thoroughly mixed until a homogenous blend is achieved. Vigorous mixing is not recommended. The mixed coating should be allowed to settle for 30 minutes prior to use so that any air bubbles formed during blending can escape.

Dipping
Depending on the complexity, density and configuration of components on the assembly, it may be necessary to reduce the viscosity of prepared HumiSeal® 2A64 with HumiSeal® Thinner 64 in order to obtain a uniform film. Once optimum viscosity is determined, a controlled rate of immersion and withdrawal (5-15 cm/min) will further ensure even deposition of the coating and ultimately a uniform film. During the application, evaporation of solvent causes an increase in viscosity that should be adjusted by adding small amounts of HumiSeal® Thinner 64. Viscosity in the dip tank should be checked regularly, using a simple measuring device such as a Zahn or Ford viscosity cup.

Spraying
HumiSeal® 2A64 can be sprayed using conventional spraying equipment. Spraying should be done in an environment with adequate ventilation so that the vapor and mist are carried away from the operator. The addition of HumiSeal® Thinner 64 is necessary to ensure a uniform spray pattern resulting in pinhole-free film. The amount of thinner and spray pressure will depend on the specific type of spray equipment used and operator technique. The recommended ratio of prepared HumiSeal® 2A64 to HumiSeal® Thinner 64 is 1:1 by volume; however, the ratio may need to be adjusted to obtain a uniform coating.

Brushing
HumiSeal® 2A64 may be applied by brush. Uniformity of the film depends on component density and the operator’s technique.

Properties of Mixed HumiSeal® 2A64
Density, per ASTM D1475 1.07 ± 0.03 g/cm3
Solids Content, % by weight per Fed-Std-141, Meth. 4044 55 ± 5 %
Viscosity, per Fed-Std-141, Meth. 4287 130 ± 50 centipoise
VOC 501 grams/litre
Recommended Coating Thickness 25 – 75 microns
Drying Time to Handle per Fed-Std-141, Meth. 4061 15 minutes
Optional Curing Conditions to Reach Optimum Properties 3 hrs @ 76°C
Recommended Thinner HumiSeal® Thinner 64
Recommended Stripper HumiSeal® Stripper 1072
Pot Life at Room Temperature 8 hours
Shelf Life at Room Temperature, DOM 12 months
Thermal Shock, 50 cycles per MIL-I-46058C -65°C to 125°C
Coefficient of Thermal Expansion – TMA 82 ppm/°C Below Tg
255 ppm/°C Above Tg
Glass Transition Temperature – DSC 12°C
Modulus – DMA 4101 MPa @ -40ºC
2777 MPa @ 25ºC
2 MPa @ 80ºC
Flammability, per MIL-I-46058C Self-Extinguishing
Dielectric Withstand Voltage, per MIL-I-46058C >1500 volts
Dielectric Breakdown Voltage, per ASTM D149 3500 volts
Dielectric Constant, at 1MHz and 25°C per ASTM D150-98 3.5
Dissipation Factor, at 1MHz and 25°C per ASTM D150-98 0.024
Insulation Resistance, per MIL-I-46058C 4.5 x 1014  ohms (450TΩ)
Moisture Insulation Resistance, per MIL-I-46058C 4.8 x 1010 ohms (48GΩ)
Fungus Resistance, per ASTM G21 Passes